20mm X 1.5mm Kovar Seamless Alloy Tube | Low CTE Matched to Borosilicate Glass for Hermetic Sealing
|
Λεπτομέρειες:
Πληρωμής & Αποστολής Όροι:
|
Λεπτομερής Περιγραφή Προϊόντος
| Ονομα: | 4J29 29Hχ BJ Kovar Glass Sealing Scaroy Nilo K | Υλικό: | Feni29co17 |
|---|---|---|---|
| Σχήμα Παροχής: | Ράβδος/σωλήνα/πλάκα/σύρμα/λωρίδα | Μέσος συντελεστής γραμμικής επέκτασης (10-6): | 4.6-5.2 (200-400 ℃) |
| Θερμοκρασία: | 435 ℃ | Μέγεθος: | 30mmx1.5mmx1500mm |
20mm X 1.5mm Kovar Seamless Alloy Tube | Low CTE Matched to Borosilicate Glass for Hermetic Sealing
Iron-nickel-cobalt alloy 4J29 alloy is also called Kovar alloy. 4J29 has a linear expansion coefficient close to that of silicon boron hard glass at 20 ° C to 450 ° C, which can be matched with hard glass to achieve sealing firmly. It has a high Curie point and has good low temperature tissue stability.
4J29 is mainly used for the glass sealing of electric vacuum components such as launch tubes, oscillation tubes, ignition tubes, magnetrons, transistors, sealed plugs, relays, integrated circuits, chassis, housings, brackets, etc.
4J29 Kovar Chemical Composition(%)
| Grade | C | Si | Mn | P | S | Ni | Co | Fe | Cu | Cr | Mo |
| 4J29 | ≤0.03 | ≤0.3 | ≤0.5 | ≤0.02 | ≤0.02 | 28.5-29.5 | 16.8-17.8 | Balance | ≤0. 2 | ≤0. 2 | ≤0. 2 |
When the average linear expansion coefficient reaches the standard stipulated conditions, the content of nickel and cobalt is allowed to deviate from the range specified in the table. The contents of aluminum, magnesium, zirconium and titanium are each not more than 0.10%, and the total amount should not be more than 0.20%
4J29 Kovar Linear Expansion Coefficient:
| Temperature Range | 20~100℃ | 20~300℃ | 20~400℃ | 20~450℃ | 20~500℃ | 20~600℃ | 20~700℃ |
| Average Linear Expansion Coefficient (10-6) |
5.8 |
5.3 |
4.6-5.2 |
5.1-5.5 |
6.2 |
7.8 |
9.2 |
4J29 Kovar Physical Properties:
| Density | 8.17g/cm3 |
| Curie Temp | 435℃ |
| Melting Point | 1449℃ |
| Thermal Conductivity | 0.17 W/cm °C |
| Tensile Strength | >518 MPa |
| Elongation | >30% |
| Hardness | >80HRB |
| Modulus of Elasticity | 30 Mpsi |
Supply Sate:
1. Sheet and foil (within a width of 2 meters)
Delivery status: hot rolled or cold rolled, annealed, pickled
2. Round plates and rings
Delivery status: hot rolled or cold rolled, annealed, pickled or machined
3. Wire
Delivery status: bright brushed, Hard, 1 / 4Hard, 1 / 2Hard, Soft
Specification: φ0.01-15mm, coiled, wrapped around a shaft or in roll form
4. Bar
Supply status: forged material, hot rolled material, cold drawn material, annealed state, pickled, machined or polished.
5. Forging
Delivery status: irregularly shaped forgings are provided upon request
6. Strip material (within 650mm, commonly used are 100mm, 150mm, 200mm, 300mm, 350mm)
Delivery status: 0.01mm-5.0mm, cold rolled, annealed, pickled or bright annealed
7. Flat wire, strip
4J29 Other Names Called International:
29HК / Kovar / Nilo K / KV-1 / Dilver P0 / Vacon 12 / 29HК-BИ / Rodar KV-2 / Techallony Glasseal 29-17 / Telcaseal KV-3 Dilver P1 / Silvar 48
Στοιχεία επικοινωνίας
Ohmalloy Material Co.,Ltd
Υπεύθυνος Επικοινωνίας: Mr. Qiu
Τηλ.:: +8613795230939
Στείλετε το ερώτημά σας απευθείας σε εμάς
Περισσότεροι χαμηλά κράματα επέκτασης
-
Χαμηλό κράμα 1,2 νικελίου σιδήρου επέκτασης Invar Φε-Ni36 4J36 ppm°C αντιδιαβρωτικό
-
γυαλί 4J29 Kovar FeNi29Co17 που σφραγίζει τα χαμηλά κράματα επέκτασης
-
Χαμηλό γυαλί λουρίδων κραμάτων 4J29 επέκτασης Kovar - - σφραγίδα μετάλλων για τις λάμπες φωτός
-
Φε-42Νι κράμα ταινία 4J42 Ύψιστης ακρίβειας ταινία Ελεγχόμενο στρώμα οξείδωσης Ερμητική συσκευασία και σφραγίδες αισθητήρων
-
Πλάκα Invar 4J36 (UNS K93600) με σχεδόν μηδενικό CTE (Συντελεστής Θερμικής Διαστολής) - Εφαρμογές Ακριβούς Μετρολογίας και Κρυογενικής
-
Σύνθεση 42 FeNi42 ταινία σφράγισης για σφράγιση γυαλιού από κεραμική σε μέταλλο